Achieving Negatively Charged Pt Single Atoms on Amorphous Ni(OH)2 Nanosheets with Promoted Hydrogen Absorption in Hydrogen Evolution

Highlights Pt–Ni bonded Pt single-atom (SA) catalyst, rather than classic Pt–O bonded SA catalyst, was successfully constructed. The electronic states of Pt SA catalyst were deeply regulated and negatively charged Ptδ− was realized. Pt–Ni bonded Pt SA catalyst-enhanced absorbability for activated hydrogen atoms and promoted hydrogen absorption. Supplementary Information The online version contains supplementary material available at 10.1007/s40820-024-01420-6.


Introduction
Hydrogen evolution reaction (HER), as a half-reaction of water electrolysis, provides a practical way to produce hydrogen with excellent energy conversion efficiency, arousing great interest in the exploration and development of highly active catalysts [1][2][3][4].Among all the catalysts, noble metal-based catalysts represented by Pt demonstrate excellent specific activity and selectivity, which are widely used in HER [5][6][7].As the scarce reserves and expensive prices seriously limit their scaling up, single-atom (SA) catalysts with the maximum atomic utilization, afford an alternative for the application of noble metal-based catalysts [8][9][10].However, in order to fix the metal atoms and prevent the agglomeration, most of the reported SA catalysts were strongly bonded with the nonmetal atoms (O, N, etc.) of the substrate [11][12][13].It will inevitably lead to the oxidation of the metal atoms and further hinder the regulation of the electronic states, diminishing their electrocatalytic properties.For example, oxidized noble metal atoms would reduce the adsorption capacity for hydrogen atoms, limiting the HER activity of the catalysts [11].
Unlike widely used crystalline substrates, amorphous materials demonstrate advantages as substrates in optimizing the geometrical and electronic structure of SA due to their unique longrange disordered and isotropic structural features [14][15][16][17][18][19].The disordered adjacent atoms on the amorphous substrates could geometrically change the active sites and rearrange the distribution of electrons, which may accelerate the charge transfer between active centers, and enhance the electrochemical activity of the active sites [11,20,21].Meanwhile, the abundant dangling bonds and defects in the amorphous substrate can anchor the SA and effectively improve the structural stability of SA catalysts in long-term service [22][23][24].The key point is that the highly coordination unsaturated local environment of exposed metal atoms on the surface of amorphous substrate could provide the possibility of constructing metal-metal bonding, instead of the conventional metal-nonmetal bonding for SA loading [7,8,25].The novel structure could subversively modulate the electronic structure of the SA catalysts, further promoting the catalytic performance [20].
Here, we report a novel Pt SA catalyst fixed by Pt-Ni bonding on amorphous Ni(OH) 2 nanosheet arrays through a controllable electrochemical reduction strategy.The coordination unsaturated atomic structure of amorphous substrate provides sufficient sites for the adsorption of PtCl

Synthesis of Ni(acac) 2 Nanosheet Arrays
30 mg of Ni(acac) 2 •2H 2 O was placed in a 100 mL flask and 30 mL of anisole was added, followed by a water bath for 1 h to accelerate the dissolution of Ni(acac) 2 •2H 2 O.And then 1 × 2 cm 2 of carbon fiber paper (CFP) was added to the solution and the flask was moved into an oil bath at 120 °C for 2 h.After that, the CFP was taken out and washed with ethanol several times.

Synthesis of a-Ni(OH) 2 Nanosheet Arrays
The constant current activation method was used to transform Ni(acac) 2 nanosheet arrays into amorphous Ni(OH) 2 (a-Ni(OH) 2 ) nanosheet arrays by removing the 1 3 organic groups.In a two-electrode system, the as-prepared nanosheet arrays was employed as the anode and the constant current electrolysis was conducted under a constant current of 5 mA in a 1 M KOH solution for 5-6 h.

Synthesis of Pt-SA/a-Ni(OH) 2
Electroplating was used for the synthesis of single-atom Pt on the a-Ni(OH) 2 nanosheet arrays (Pt-SA/a-Ni(OH) 2 ).In a typical experiment, the a-Ni(OH) 2 was served as the cathode, together with a carbon rod as the counterpart electrode and Hg/HgO electrode as the reference electrode, and then placed in a 1 M KOH solution containing 10 −5 M PtCl 6 2− solution.Constant voltage electrolysis was conducted at −0.079 V vs. RHE for 20 min, during which the platinum in the solution is reduced and plated onto the a-Ni(OH) 2 nanosheet arrays.

Synthesis of Pt-NP/a-Ni(OH) 2
The reference material was synthesis in a similar method with Pt-SA/a-Ni(OH) 2 .For the synthesis of nanoparticle Pt on a-Ni(OH) 2 nanosheet arrays, the electroplating time was 40 min, with other parameters remaining the same in the synthesis of Pt-SA/a-Ni(OH) 2 .

Preparation of Pt/C Catalyst
20 mg of commercial Pt/C (20 wt%) catalyst was dispersed in 990 µL of ethanol, followed by the addition of 10 µL of 5 wt% nafion solution.After 20 min of sonication, a homogeneous ink was obtained.Finally, 100 µL of ink was pipetted to the CFP (1 × 1 cm 2 ) on both sides for even coating, and dried in air.

Preparation of Pt/CFP
The reference material was synthesized in a similar method with Pt-SA/a-Ni(OH) 2 .For the synthesis of Pt on CFP (Pt/ CFP), the substrate for electroplating was the bared carbon fiber paper.And the parameters of electroplating were the same with those in the synthesis of Pt-SA/a-Ni(OH) 2 .In a typical experiment, the loading amount of Pt in Pt/CFP is tested to be 0.15%.

Synthesis of Pt-SA/commercial Ni(OH) 2
For the synthesis of single atom Pt on commercial Ni(OH) 2 (Pt-SA/commercial Ni(OH) 2 ), 5 mg of commercial Ni(OH) 2 was dispersed in 990 µL of ethanol, followed by the addition of 10 μL of nafion solution.The prepared Ni(OH) 2 ink was dropped onto a CFP (1 × 2 cm 2 ).Next, this CFP was used as the working electrode and the electroplating of single atom Pt was conducted.The parameters of electroplating were the same with those in the synthesis of Pt-SA/a-Ni(OH) 2 .

Morphology of Pt-SA/a-Ni(OH) 2
β-Ni(OH) 2 demonstrates a stratified structure connected by Ni-O 6 octahedrons as units, with hydroxyl groups facing outwards [26].Thus, when it is employed as the substrate to construct SA catalysts, the loaded metal atoms can only be coordinated with oxygen atoms.In contrast, the amorphous Ni(OH) 2 presents a large number of unsaturated Ni sites with oxygen vacancies [27], which provide an ideal platform for the establishment of single metal atom bonding to Ni sites (Fig. 1a).The substrate was constructed in two steps.Firstly, Ni(acac) 2 nanosheet arrays were grown on carbon fibers (Fig. 1b); secondly, amorphous Ni(OH) 2 nanosheet arrays were generated through the electrochemical transformation from Ni(acac) 2 nanosheet arrays (Fig. 1c) [28].Next, Pt SA was loaded on amorphous Ni(OH) 2 nanosheet arrays (named as Pt-SA/a-Ni(OH) 2 ) by electrochemical reduction in 10 −5 M PtCl 6 2− solution at −0.079 V vs. RHE for 20 min (Fig. 1d).Transmission electron microscopy (TEM) results showed that amorphous Ni(OH) 2 nanosheets were grown vertically on carbon fibers (Fig. 1e-g), providing a large area for the deposition of Pt SA.Aberration corrected high-angle annular dark field (AC-HAADF) image showed that Ni(OH) 2 nanosheets have no obvious lattice fringes, evidencing an amorphous structure.The Pt SA as brighter spots are dispersedly loaded on amorphous Ni(OH) 2 nanosheets, without the appearance of Pt clusters or particles (Fig. 1h).The loading amount of Pt in Pt-SA/a-Ni(OH) 2 was calculated to be ~ 0.07 wt% through inductively coupled plasma optical emission spectrometer (ICP-OES) (Fig. S1).If the electrochemical reduction time was extended to more than 40 min, Pt nanoparticles (Pt-NP/a-Ni(OH) 2 ) were observed (Fig. S2), instead of single atom.The electron paramagnetic resonance (EPR) spectra of the amorphous Ni(OH) 2 nanosheets and the Pt-SA/a-Ni(OH) 2 catalyst exhibited typical signals at g = 2.003, confirming the existence of the oxygen vacancies in the system (Fig. S3).The presence of oxygen vacancies helps to stabilize Pt SA on the substrate.

Atomic Structure of Pt-SA/a-Ni(OH) 2
In order to demonstrate the atomic structure of the Pt-SA/a-Ni(OH) 2 catalyst, we then investigated the coordination environment of Pt in Pt-SA/a-Ni(OH) 2 through X-ray absorption fine structure (XAFS) analysis (Fig. 2a).In the Fourier transformed extended X-ray absorption fine structure (EXAFS) spectra (Figs.2b and S4, Table S1), the Pt foil exhibited a clear Pt-Pt bond at 2.  Pt-SA/a-Ni(OH) 2 is basically the same as that of Pt in the Pt-Ni alloy, which proves the bond of Pt-Ni in Pt-SA/a-Ni(OH) 2 catalyst (Fig. S6).Similarly, the Pt-Ni bond can be directly observed as the dominant form of Pt present in this system through wavelet transformations [34], rather than the Pt-Pt bond of bulk Pt or the Pt-O bond for conventional Pt SA materials (Fig. 2c-f).
To further verify Pt-Ni bonding in the catalyst, X-ray photoelectron spectroscopy (XPS) characterization was employed to perform series of supported Pt catalysts Pt-SA/a-Ni(OH) 2 with the local environment of Pt-Ni bonding, the Pt atom with greater electron-negative can take electrons from Ni atoms and thus became partially negatively charged.When the electrodeposition time increased, Pt species transforms from SA to particle, and the Pt-Pt bonds take advantages, making its valence state closer to 0 valence.
The novel electronic states of Pt SA were further confirmed by DFT calculations.It demonstrated that when Pt SA was adsorbed onto the Ni(OH) 2 substrate with oxygen vacancies, the three Ni atoms bonded with the Pt SA.As shown in Figs.3d, e and S9, the charge transfer occurred between Pt SA and the Ni(OH) 2 substrate, resulting in electron gain by the Pt atoms and manifestation of a negatively charged state, aligning with the experimental XPS results.To unravel the underlying mechanisms for the enhanced HER performance within the Pt SA, we conducted a systematic analysis of the electronic structure of the Pt atom under various hydrogen adsorption scenarios on the Pt SA on Ni(OH) 2 substrate (Figs.3f and S10a).When H adsorption on the Pt-SA, the negative charged Pt donates about 0.11 e to first H atom based on the Bader charge, as shown in Table S2.As discussed above, the Pt behaves as negative charge for the whole process.Thus, the electronic structure of Pt-Ni model is greatly different from the counterpart of Pt-O.As shown in Fig. S10b and Table S3, the Pt of Pt-O system tends to accept a small amount of electrons from Ni(OH) 2 by about −0.03 e. Upon H adsorption, the Pt donates electron to H and Ni(OH) 2 , which makes Pt as positive charge (0.28 e).The calculated density of states (DOS) unveiled that upon hydrogen atoms adsorption onto Pt SA, the extra electrons, donated by the Ni(OH) 2 substrate to the Pt SA, could transfer to the hydrogen atoms, thus actively promoting the HER process.Consequently, the Ni-bonded Pt SA structure stands as a catalyst with remarkable efficiency in advancing the HER process.

HER Mechanisms of Pt-SA/a-Ni(OH) 2 Catalyst
Compared to traditional Pt-O bonded Pt SA, Pt-Ni bonded Pt SA has a lower oxidation state, making them more favorable for adsorption of activated hydrogen atoms in the electrolyte, especially under the alkaline [11,32].Compared to the widely studied HER in the acidic, the HER under alkaline conditions has milder reaction conditions and higher energy conversion efficiency [35,36].However, due to the absence of H + in the solution, the water dissociation step of the HER under alkaline medium is slow and the proton supply is poor, making its rate several orders of magnitude lower than that in acidic medium [37][38][39].In order to explore the structural advantages of the Pt-SA/a-Ni(OH) 2 catalyst for alkaline HER and the possible reaction mechanisms, the adsorbed species of the catalysts during the catalytic reaction was detected by in situ Raman spectroscopy (Fig. S11).As shown in the Raman spectra of Fig. 4a, there is no Pt-H stretching vibration signal at ~ 2170 cm −1 before applying voltage [40].After applying a negative potential for starting HER, a significant Pt-H vibration appeared at ~ 2170 cm −1 , and the intensity of the peak enhanced synchronously with the increase of the applied negative voltage.It demonstrated the strong adsorption capacity and responsivity of hydrogen for the Pt site in Pt-SA/a-Ni(OH) 2 , consistent with our speculation that Pt-Ni bonding enhances adsorption for hydrogen atoms.
Apart from Pt-H stretching vibration, another additional peak at ~ 1630 cm −1 was also observed in Raman spectra when a negative potential was applied.It was attributed to the H-O-H bending vibration [41].With the increase of the applied negative potential, this peak was also enhanced synchronously, which means that the adsorption of water was also promoted by the catalyst during the HER process.This promotion was also confirmed on pure amorphous Ni(OH) 2 substrate, demonstrating the enhanced adsorption of H 2 O molecule on amorphous Ni(OH) 2 (Fig. S12).According to previous report, Ni(OH) 2 can cleave the H-O-H bond of H 2 O at the interface of Ni(OH) 2 and Pt, producing hydrogen atoms and transferring them to the active sites for HER reactions [42,43].Combined with the synchronously enhanced Pt-H bond, we supposed that amorphous Ni(OH) 2 can accelerate water dissociation process.The generated H ad intermediates transferred to the Pt SA immediately afterward and thus facilitated HER.To validate this hydrogen spillover process, the in situ Raman spectra of commercial Pt/C in HER was also performed (Fig. 4b) [37,44].It was found that the H-O-H bending vibrational signal could not be observed at 1630 cm −1 , even when a negative voltage was applied.It indicated that compared with amorphous Ni(OH) 2 , the adsorption of water molecules is weak for commercial Pt/C.Meanwhile, almost imperceptible Pt-H stretching vibration was exhibited at ~ 2170 cm −1 .It suggested that the amorphous Ni(OH) 2 substrate effectively adsorbed and cleaved water molecules, providing a large number of H ad intermediates for the Pt SA and thus promoting HER (Fig. 4c).Based on the first-principles molecular dynamics (FPMD) simulations, the extra H transfer from Ni(OH) 2 to Pt was observed for 1.73 ps, indicating that H transfer could occur between Ni(OH) 2 and Pt for the model of Pt over Ni atom of Ni(OH) 2 , while the H transfer is not observed for the Pt adsorption over the oxygen atom of Ni(OH) 2 for the same FPMD setups (Fig. S13, Movies S1, S2).
DFT calculations were performed to investigate the connection between the material structures and HER performance, and the calculated Gibbs free energy of hydrogen adsorption (ΔG H ) were shown in Fig. 4d.The HER performance could be evaluated by the absolute value of ΔG H , as proposed by by Nørskov [45].According to the calculated results, compared with the traditional Pt-O based SA catalysts and Pt NP catalysts, Ni-bonded Pt SA shows the lowest ΔG H , indicating the high HER activity (Figs.S14-S16).Furthermore, after the first hydrogen atom has adsorbed on the Pt site, the ΔG H of Ni-bonded Pt*H SA for the next H adsorption process decreases to be as small as 0.09 eV (Fig. S14).Therefore, the Ni-bonded Pt SA catalyst could exhibit an excellent catalytic performance of HER.5a).This overpotential is significantly lower than that of the a-Ni(OH) 2 substrate and the other comparative samples with different types of Pt-based bonds (Figs.5a and  S17), which is also comparable to some recently reported Pt based works (Table S4) [5,8,[46][47][48][49].Furthermore, normalized the mass of Pt, its overpotential is only 48 mV at −1000 mA cm −2 mg −1 Pt , which is considerably lower than the overpotential of commercial Pt/C of 128 mV (Figs.5b  and S18).The remarkable performance should be attributed to the above mentioned SA of Pt-Ni bonding configuration and its synergistic effect with the amorphous substrates.To confirm the HER mechanism, we conducted the kinetic process of the reaction through calculating the value of Tafel slope (Fig. 5c).The Tafel slope of 46 mV dec −1 for Pt-SA/a-Ni(OH) 2 is much lower than those of Pt/CFP and Pt-NP/a-Ni(OH) 2 , indicating that the Volmer step of water dissociation in alkaline HER was accelerated in the Pt-SA/a-Ni(OH) 2 , in agreement with the Raman spectra results.In addition, the durability of Pt-SA/a-Ni(OH) 2 catalyst was also evaluated through chronoamperometry (CA) test, which showed that the catalyst kept excellent stability during 150 h of HER (Fig. 5d).The morphology and atomic structure were also well maintained (Fig. S19).

Conclusion
In summary, utilizing the exposed Ni sites with oxygen vacancies on amorphous Ni(OH) 2 to anchor Pt, Pt-Ni bonding fixed Pt SA are constructed, instead of Pt-O bonding in the conventional Pt SA catalysts.The novel structure greatly facilitates alkaline HER process by both the unique atomic and electronic structures.The amorphous Ni(OH) 2 substrate effectively adsorbs and cleaves water molecules, accelerating the Volmer step of water dissociation in alkaline HER and providing H ad for the Pt site.Furthermore, the Pt-Ni bond reduces the oxidation state of the Pt SA and thus optimize the adsorption capacity for hydrogen atoms.This work provides a new idea to deeply modulate the configuration of SA catalysts and thus controllably regulate the electronic states of SA catalysts to enhance catalytic performance.
5 Å, and the bond was almost unrecognizable in the Pt-SA/a-Ni(OH) 2 sample, confirming the single atom state of Pt[29][30][31].At the same time, the main peak of Pt-SA/a-Ni(OH) 2 catalyst located at 2.3 Å was also distinguishing from Pt-O bond of standard Pt-O 2 at 1.6 Å[32,33].It meant that Pt-SA/a-Ni(OH) 2 catalyst displayed a different structure from the conventional SA materials based on Pt-O bonding, which we have also synthesized by employing commercially crystalline Ni(OH) 2 as a substrate (Fig.S5).It is interesting that the Pt signal in

Fig. 4 3 3. 4 HER
Fig. 4 Strong adsorption capacity of hydrogen for the Pt site in Pt-SA/a-Ni(OH) 2 .a In situ Raman spectra of Pt-SA/a-Ni(OH) 2 during HER.b In situ Raman spectra of commercial Pt/C during HER.c Schematic diagram of the hydrogen spillover processes at Pt-SA/a-Ni(OH) 2 during HER.d ΔG H of Pt-O-SA, Ni-bonded Pt SA, Ni-bonded Pt*1H SA and Pt(111).Pt(111) is regarded as a simplified model for Pt NP in Pt/C

Fig. 5
Fig. 5 HER performance of Pt-SA/a-Ni(OH) 2 .a LSV curves of Pt-SA/a-Ni(OH) 2 catalyst and the comparative samples.b Pt normalized LSV curves of Pt-SA/a-Ni(OH) 2 catalyst and commercial Pt/C.c Tafel slopes of Pt/CFP, Pt-SA/a-Ni(OH) 2 catalyst, Pt-NP/a-Ni(OH) 2 catalyst.d Stability of Pt-SA/a-Ni(OH) 2 evaluated through CA test 6  2−ions, while the nascent Pt SA from reduction is captured by the exposed Ni metal sites at the oxygen vacancies to form Pt-Ni bonds instead of the conventional Pt-O bonds.Both of the density functional theory (DFT) calculation and in situ Raman spectroscopy demonstrate the enhanced absorbability for activated hydrogen atoms, which facilitates hydrogen spillover processes between amorphous Ni(OH) 2 substrate and Pt SA in the alkaline.The amorphous Ni(OH) 2 substrate efficiently cleaves water molecules and delivers hydrogen atoms to the Pt sites, significantly increasing the hydrogen coverage on the Pt SA and leading to the enhanced HER performance.This work provides a method for the development of highly active SA catalysts, which could efficiently promote the hydrogen production in alkaline solution.